Protective SILVER-BRITE HEAVY DUTY

Protective SILVER-BRITE® HEAVY DUTY
&
RUST RESISTANT ALUMINUM PAINT
Marine
Coatings B59S2

Revised: March 27, 2014 2.42

PRODUCT DESCRIPTION RECOMMENDED USES

SILVER-BRITE HEAVY DUTY RUST RESISTANT ALUMINUM For use over prepared steel surfaces in normal and high tempera-
PAINT is a superior quality, one package, interior/exterior aluminum ture (up to 400°F/204°C) environments.
paint formulated with 325 mesh leafing aluminum pigment to give
excellent rust inhibition and heat resistance up to 400°F (204°C). • Interior / exterior • Radiators
• Bridges • Refineries
• Excellent weathering characteristics • Fences • Siding
• Maintains aluminum appearance • Metal roofs • Insulation
• Brush, roll, or spray application • Piping • Storage tank exteriors
• Stacks • Industrial mufflers

Finish: PRODUCT CHARACTERISTICS PERFORMANCE CHARACTERISTICS

Aluminum Sheen • Brilliant aluminum appearance

Color: Aluminum • Ultraviolet light resistant

Volume Solids: 39% ± 2% • Long term corrosion protection against weathering and
moisture
Weight Solids: 48% ± 2%
• Heat reflective
VOC (EPA Method 24): <480 g/L, 4.0 lb/gal
• Dry heat resistant to 400°F (204°C)
Recommended Spreading Rate per coat:
Provides performance comparable to products formulated to
Wet mils (microns) Minimum Maximum specification: AASHT0-M69-70
Dry mils (microns) 3.0 (75)
~Coverage sq ft/gal (m2/L) 1.0 (25) 4.0 (100)
Theoretical coverage sq. ft/gal 416 (10.1) 1.5* (40)*
(m2/L) @ 1 mil / 25 microns dft 624 (15.3)
624 (15.3)
*Critical

Drying Schedule @ 3.0 mils wet (75 microns):

@ 50°F/10°C @ 77°F/25°C @ 100°F/38°C

50% RH

To touch: 4 hours 30 minutes 20 minutes

Tack free: 10 hours 6-8 hours 2 hours

To recoat: 22 hours 18 hours 4 hours

To cure: 30 days 30 days 4 days

Drying time is temperature, humidity, and film thickness dependent.

Shelf Life: 36 months, unopened
Store indoors at 50°F (10°C) to
Flash Point: 100°F (38°C).
Reducer:
Clean Up: 105°F (40°C), PMCC

Not recommended

Mineral Spirits, R1K4

continued on back

Protective SILVER-BRITE® HEAVY DUTY
&
RUST RESISTANT ALUMINUM PAINT
Marine
Coatings B59S2

PRODUCT INFORMATION 2.42

RECOMMENDED SYSTEMS SURFACE PREPARATION

Dry Film Thickness / ct.

Mils (Microns) Surface must be clean, dry, and in sound condition. Remove all
oil, dust, grease, dirt, loose rust, and other foreign material to
Steel, 200°F (93°C) - 400°F (204°C): 1.0-1.5 (25-40) ensure adequate adhesion.
2 cts. Silver-Brite Heavy Duty Rust
Refer to product Application Bulletin for detailed surface prepara-
Resistant Aluminum Paint tion information.

Steel, new or rusted, below 200°F (93°C): Minimum recommended surface preparation:
Iron & Steel: SSPC-SP6/NACE 3, 1 mil profile <200°F
1 ct. Kem Bond HS 2.0-5.0 (50-125)
(25-40) (93°C)
1-2 cts. Silver-Brite Heavy Duty Rust 1.0-1.5
SSPC-SP10/NACE 2, 1 mil profile >200°F

Resistant Aluminum Paint (93°C)

* Aluminum SSPC-SP1

* Galvanizing: SSPC-SP1

Aluminum, below 200°F (93°C): * Concrete & Masonry: SSPC-SP13/NACE 6 or ICRI No. 310.2,
1 ct. DTM Wash Primer
2 cts. Silver-Brite Heavy Duty Rust 0.7-1.3 (18-32) CSP 1-3
1.0-1.5 (25-40)
Resistant Aluminum Paint * Primer required

Surface Preparation Standards

Condition of ISO 8501-1 Swedish Std.
Surface BS7079:A1 SIS055900 SSPC NACE
SP 5 1
Concrete, below 200°F (93°C): White Metal Sa 3 Sa 3 SP 10 2
1 ct. Heavy Duty Block Filler Near White Metal Sa 2.5 Sa 2.5 SP 6 3
1-2 cts. Silver-Brite Heavy Duty Rust Commercial Blast Sa 2 Sa 2 SP 7 4
10.0-18.0 (250-450) Brush-Off Blast Sa 1 Sa 1 SP 2 -
Resistant Aluminum Paint 1.0-1.5 (25-40) Rusted C St 2 C St 2 SP 2 -
Hand Tool Cleaning Pitted & Rusted D St 2 D St 2 SP 3 -
C St 3 SP 3 -
Power Tool Cleaning Rusted Rusted C St 3 D St 3
Pitted & D St 3

Galvanized Metal, below 200°F (93°C): TINTING

1 ct. Galvite HS 3.0-4.5 (75-112)
(25-40)
1-2 cts. Silver-Brite Heavy Duty Rust 1.0-1.5 Do not tint.

Resistant Aluminum Paint APPLICATION CONDITIONS

Insulated Pipe and Ductwork, interior below 130°F (54°C): Temperature: 50°F (10°C) minimum, 120°F (49°C)
1 ct. Loxon Concrete & Masonry Primer 2.1-3.2 (52.5-80) Relative humidity: maximum
1-2 cts. Silver-Brite Heavy Duty Rust 1.0-1.5 (25-40) (air, surface, and material)
At least 5°F (2.8°C) above dew point
Resistant Aluminum Paint 85% maximum

Masonry, below 200°F (93°C)-Exterior: Refer to product Application Bulletin for detailed application information.
1 ct. Loxon Concrete & Masonry Primer 2.1-3.2
1-2 cts. Silver-Brite Heavy Duty Rust 1.0-1.5 (52.5-80) ORDERING INFORMATION
(25-40)
Resistant Aluminum Paint

Masonry, below 200°F (93°C)-Interior: (52.5-80) Packaging: 1 gallon (3.78L) and 5 gallon (18.9L)
1 ct. Loxon Concrete & Masonry Primer 2.1-3.2 (25-40) Weight: containers
1-2 cts. Silver-Brite Heavy Duty Rust 1.0-1.5 7.75 ± 0.2 lb/gl, .93 Kg/L

Resistant Aluminum Paint SAFETY PRECAUTIONS

Refer to the MSDS sheet before use.

The systems listed above are representative of the product's use, Published technical data and instructions are subject to change without notice.
other systems may be appropriate. Contact your Sherwin-Williams representative for additional technical data and
instructions.

DISCLAIMER WARRANTY

The information and recommendations set forth in this Product Data Sheet are The Sherwin-Williams Company warrants our products to be free of manufactur-
based upon tests conducted by or on behalf of The Sherwin-Williams Company. ing defects in accord with applicable Sherwin-Williams quality control procedures.
Such information and recommendations set forth herein are subject to change and Liability for products proven defective, if any, is limited to replacement of the defec-
pertain to the product offered at the time of publication. Consult your Sherwin- tive product or the refund of the purchase price paid for the defective product as
Williams representative to obtain the most recent Product Data Information and determined by Sherwin-Williams. NO OTHER WARRANTY OR GUARANTEE
Application Bulletin. OF ANY KIND IS MADE BY SHERWIN-WILLIAMS, EXPRESSED OR IMPLIED,
STATUTORY, BY OPERATION OF LAW OR OTHERWISE, INCLUDING MER-
CHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE.

Protective SILVER-BRITE® HEAVY DUTY
&
RUST RESISTANT ALUMINUM PAINT
Marine
Coatings B59S2

Revised: March 27, 2014 APPLICATION BULLETIN 2.42

SURFACE PREPARATIONS Temperature: APPLICATION CONDITIONS

Surface must be clean, dry, and in sound condition. Remove all 50°F (10°C) minimum, 120°F (49°C)
oil, dust, grease, dirt, loose rust, and other foreign material to maximum
ensure adequate adhesion. (air, surface, and material)
At least 5°F (2.8°C) above dew point

Iron & Steel (below 200°F/93°C) Relative humidity: 85% maximum
Remove all oil and grease from surface by Solvent Cleaning per
SSPC-SP1. Minimum surface preparation is Commercial Blast APPLICATION EQUIPMENT
Cleaning per SSPC-SP6/NACE 3, 1 mil / 25 micron profile maxi-
mum. The following is a guide. Changes in pressures and tip sizes may
be needed for proper spray characteristics. Always purge spray
Iron & Steel (200°F/93°C - 400°F/204°C) equipment before use with listed reducer. Any reduction must be
Remove all oil and grease from the surface by Solvent Cleaning compliant with existing VOC regulations and compatible with the
per SSPC-SP1. Minimum surface preparation is Commercial existing environmental and application conditions.
Blast Cleaning per SSPC-SP6/NACE 3, 1 mil / 25 micron profile
maximum. Apply 2 coats Silver-Brite Heavy Duty Rust Resistant Reducer ...........................Not recommended
Aluminum Paint.
Clean Up ..........................Mineral Spirits, R1K4
Aluminum
Remove all oil, grease, dirt, oxide and other foreign material by Airless Spray
Solvent Cleaning per SSPC-SP1. Primer required. Pressure.........................2000 psi
Hose...............................1/4" ID
Concrete/Masonry (below 200°F/93°C) Tip ...................................011"-.015"
For surface preparation, refer to SSPC-SP13/NACE 6 or ICRI No. Filter ...............................60 mesh
310.2, CSP 1-3. Surface should be thoroughly clean and dry. Air,
surface, and material temperature must be at least 55°F (13°C) Conventional Spray
before filling. Use Heavy Duty Block Filler. The filler must be Gun ................................Binks 95
thoroughly dry before topcoating per manufacturer's recommenda- Fluid Nozzle ...................63C
tions. Primer required. Air Nozzle.......................63PB
Atomization Pressure.....50 psi
Galvanized Metal (below 200°F/93°C) Fluid Pressure................20 psi
Allow to weather a minimum of six months prior to coating. Solvent
Clean per SSPC-SP1. Prime with Galvite HS. When weathering Brush
is not possible, or the surface has been treated with chromates or Brush..............................Natural Bristle
silicates, first Solvent Clean per SSPC-SP1 and apply a test patch
of primer coat. Allow paint to dry at least one week before testing Roller
adhesion. If adhesion is poor, brush blasting per SSPC-SP7 is nec- Cover .............................3/8" woven with solvent resistant core
essary to remove these treatments. Rusty galvanizing below 200°F
(93°C) requires a minimum of Hand Tool Cleaning per SSPC-SP2. If specific application equipment is not listed above, equivalent
Prime rusty areas with Galvite HS. equipment may be substituted.

Insulated Pipe & Ductwork (interior below 130°F/54°C)

Prime with PrepRite 200 Latex Wall Primer.

NOTE: For insulated pipe and ductwork 130°F (54°C) to 400°F

(204°C), apply 2 coats Silver-Brite Aluminum Paint directly to

prepared surface.

Surface Preparation Standards

Condition of ISO 8501-1 Swedish Std. NACE
Surface BS7079:A1 SIS055900 SSPC 1
SP 5 2
White Metal Sa 3 Sa 3 SP 10 3
Near White Metal Sa 2.5 Sa 2.5 SP 6 4
Commercial Blast Sa 2 Sa 2 SP 7 -
Brush-Off Blast Sa 1 Sa 1 SP 2 -
Rusted C St 2 C St 2 SP 2 -
Hand Tool Cleaning Pitted & Rusted D St 2 D St 2 SP 3 -
C St 3 SP 3
Power Tool Cleaning Rusted Rusted C St 3 D St 3
Pitted & D St 3

continued on back

Protective SILVER-BRITE® HEAVY DUTY
&
RUST RESISTANT ALUMINUM PAINT
Marine
Coatings B59S2

APPLICATION BULLETIN 2.42

APPLICATION PROCEDURES PERFORMANCE TIPS

Surface preparation must be completed as indicated. Stripe coat all crevices, welds, and sharp angles to prevent early
Lightly stir before use. Do not shake with mechanical shaker or failure in these areas.
overly agitate, as a dull, non-uniform, mottled appearance will
result. When using spray application, use a 50% overlap with each pass
For best results, apply to a cool surface between 50°F (10°C) of the gun to avoid holidays, bare areas, and pinholes. If necessary,
-100°F (93°C). cross spray at a right angle.
Apply paint at the recommended film thickness and spreading
rate as indicated below: Spreading rates are calculated on volume solids and do not include
an application loss factor due to surface profile, roughness or po-
Recommended Spreading Rate per coat: rosity of the surface, skill and technique of the applicator, method
of application, various surface irregularities, material lost during
Minimum Maximum mixing, spillage, overthinning, climatic conditions, and excessive
film build.
Wet mils (microns) 3.0 (75) 4.0 (100)
Dry mils (microns) 1.0 (25) 1.5* (40)* No reduction of material is recommended as it can affect film build,
~Coverage sq ft/gal (m2/L) 416 (10.1) 624 (15.3) appearance, and adhesion.
Theoretical coverage sq. ft/gal
(m2/L) @ 1 mil / 25 microns dft 624 (15.3) In order to avoid blockage of spray equipment, clean equipment
before use or before periods of extended downtime with Mineral
*Critical Spirits, R1K4.

Drying Schedule @ 3.0 mils wet (75 microns): Do not apply at greater than 1.5 mils (40 microns) dft/ct.

@ 50°F/10°C @ 77°F/25°C @ 100°F/38°C For best results, apply to a cool surface between 60°F (16°C) -
90°F (32°C).
50% RH

To touch: 4 hours 30 minutes 20 minutes

Tack free: 10 hours 6-8 hours 2 hours

To recoat: 22 hours 18 hours 4 hours

To cure: 30 days 30 days 4 days

Drying time is temperature, humidity, and film thickness dependent.

Special care should be exercised while using this product for
maximum performance. Film thickness and surface preparation
are critical. Be especially concerned at lap areas and when using
airless spray. Excessive film thickness will cause blistering and
peeling. Insufficient film thickness may lead to premature rusting
of the surface.

Application of coating above maximum or below minimum Refer to Product Information sheet for additional performance
recommended spreading rate may adversely affect coating characteristics and properties.
performance.

SAFETY PRECAUTIONS

Refer to the MSDS sheet before use.

CLEAN UP INSTRUCTIONS Published technical data and instructions are subject to change without notice.
Contact your Sherwin-Williams representative for additional technical data and
Clean spills and spatters immediately with Mineral Spirits, R1K4. instructions.
Clean tools immediately after use with Mineral Spirits, R1K4. Follow
manufacturer's safety recommendations when using any solvent. WARRANTY

DISCLAIMER The Sherwin-Williams Company warrants our products to be free of manufacturing
defects in accord with applicable Sherwin-Williams quality control procedures.
The information and recommendations set forth in this Product Data Sheet are Liability for products proven defective, if any, is limited to replacement of the de-
based upon tests conducted by or on behalf of The Sherwin-Williams Company. fective product or the refund of the purchase price paid for the defective product
Such information and recommendations set forth herein are subject to change and as determined by Sherwin-Williams. NO OTHER WARRANTY OR GUARANTEE
pertain to the product offered at the time of publication. Consult your Sherwin- OF ANY KIND IS MADE BY SHERWIN-WILLIAMS, EXPRESSED OR IMPLIED,
Williams representative to obtain the most recent Product Data Information and STATUTORY, BY OPERATION OF LAW OR OTHERWISE, INCLUDING MER-
Application Bulletin. CHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE.